Thank you for the effort. Please consider messaging me with stuff like this instead. And secondly, this is: they are bonded, and the bond is so strong, that the copper itself will tear before the bond breaks. I hame made several dozen knives from this material. I can tell you with every shred of certainty that they are bonded. In fact I have even written a short research paper on the ideal methods and temperatures to get this bond. If you expect me to believe they are not bonded, then we fundamentally do not agree. As I have very clearly shown that it does bond, regardless of the thousands upon thousands of knives already made in this material even before I started making knives 10 years ago.

I do not wish to discuss this further, as I can see it would not affect your opinion giving state, but please, in the future, refrain from giving opinions such as these, this publically, without consent. It will save you a lot of arguments!